304不锈钢板的钝化处理及耐蚀性

2020年3月电镀与环保第40卷第2期(总第232期)*37-

304不锈钢板的钝化处理及耐蚀性Passivati o n Treatment and Corrosi o n Resistance o f304Stainless Steel Plate

仝源

(南京科技职业学院，江苏南京210048)

TONG Yuan

(Nanjing Polytechnic Institute,Nanjing210048,China)

摘要：使用硝酸和重珞酸钾的混合液对304不锈钢板进行了钝化处理。研究发现：不锈钢表面钝化过程伴随着钝化膜的生成和溶解。与304不锈钢板相比，钝化膜中铬和氧的质量分数提高。钝化膜主要由金属氧化物和金属氢氧化物构成。经过钝化处理后，304不锈钢板的自腐蚀电位正移，自腐蚀电流密度降低，膜电阻升高，耐蚀性增强。

关键词：304不锈钢板；钝化膜；耐蚀性

Abstract:304stainless steel plate was passivated in a mixture of nitric acid and potassium dichromate.It was found that the passivation of stainless steel was accompanied by the formation and dissolution of passivation film.Compared with304stainless steel plate,the mass fraction of chromium and oxygen in the passivation film were increased obviously.The passivation film was composed of metal oxide and metal hydroxide.After passivation treatment,the self-corrosion potential of304stainless steel moved towards the positive direction,the self-corrosion current density was decreased and the film resistance was increased,thus resulting in the improvement of corrosionresistance.

Key words：304stainless steel plate；passivation film；corrosion resistance

中图分类号：TG174文献标志码：A文章编号：10004742(2020)02003703

0前言

不锈钢是一种具有综合性能的合金钢，已广泛应用于汽车、化工、航空航天等领域X。自然条件下，不锈钢表面形成的氧化膜疏松、不均匀，防护性能较差。由于不锈钢具有良好的钝化特性，所以常采用钝化处理提高不锈钢的耐蚀性卩7。本文使用硝酸和重铬钾的混合液对304不锈钢板进行了钝化处理，并研究了钝化膜的表面形貌、成分及耐蚀性。

1实验

11钝化液组成及工艺条件

质量分数为68%的硝酸200mL/L，重铬钾30g/L，温度60f，时间15min。

1.2实验方法

基体采用尺寸为3.0cmX3.0cmX0.2cm的304不锈钢板。工艺流程为：砂纸打磨一超声波处理一烘干一&钝化一＞质量分数为5%的重铬酸钾封闭10min—质量分数为1%的氢氧化钠中和一水洗一烘干。

1.3性能测试

使用S3400N型扫描电子显微镜观察304不锈钢板和钝化膜的表面形貌。使用EDX3200S型X 射散荧光光谱仪分析304不锈钢板和钝化膜的成分。使用CHI760E型电化学工作站并结合失重试验测试钝化膜的耐蚀性。

2结果与讨论

2.1304不锈钢板的钝化机制

使用硝酸和重铬钾的混合液对304不锈钢板进行钝化处理，具体反应过程如下：

HNOs=O+NOh+H+(1)

2H++2e h=H z(2)